Wavelength 780-1029 nm
780 | 800 | 808 | 850 | 914 | 940 | 946 | 976 | 980 nm

Diode laser / Ti:Sapphire / Er:YLF/YAP / InGaAs diode / weak Nd:YAG/YVO4

NIR 780-1029 nm

Coating types
VAR
AR
  • VAR
  • DAR
  • TAR
  • BBAR
  • MAR
  • WAR
VAR
VAR
λ [nm]AR (0°); R < methodAR (45°); R < method
780 0.2%   EBE 0.6%   EBE
800 0.2%   EBE 0.6%   EBE
  0.05-0.1%* low loss IBS 0.1-0.6%* low loss IBS
808 0.2%   EBE 0.6%   EBE
940 0.2%   EBE 0.6%   EBE
  0.05-0.1%* low loss IBS 0.1-0.6%* low loss IBS

* depending on price, substrate size and laser power

HR
HR
  • HR
  • DHR
  • BBHR
  • MHR
  • WHR
  • Metal
HR
HR
λ [nm]HR (0°); R > methodHR (45°); R > method
780 99.85%   EBE 99.8%   EBE
800 99.9xxx%* low loss IBS 99.9xxx%* low loss IBS
808 99.85%   EBE 99.8%   EBE
850 99.85%   EBE 99.8%   EBE
914 99.85%   EBE 99.8%   EBE
940 99.8% standard EBE 99.75% standard EBE
  99.85% non-shifting IAD 99.8% non-shifting IAD
  99.9xxx%* low loss IBS 99.9xxx%* low loss IBS
976 99.85%   EBE 99.8%   EBE
980 99.85%   EBE 99.8%   EBE

* 99.9xxx% means that we can optimize the reflection/transmission to your needs.
The coating price results from the chosen grade of reflection/difficulty, see estimated multiplier:

 Price multiplier

TFP
POLARIZER
  • TFP
  • CP
  • BBPOL
TFP
TFP
λ [nm] AOImethod
800 Tp > 99%, Ts < 0.1% Brewster IBS
808 Tp > 95%, Ts < 1% Brewster EBE
940 Tp > 95%, Ts < 1% Brewster IAD
VA
VARIABLES
  • VA
  • GOC
  • GP
  • GNF
  • GIF
VA
VA
λ [nm]0°→ 45°; T = method
808 95% → 1% non-shifting IAD
940 95% → 1% non-shifting IAD

All values are given for standard coatings. Customized coatings available for all types.

Coating methods available:

EBEIADIPMSIBS

Examples

If not mentioned otherwise, all values and diagrams are given

... for the standard substrate material used in the described wavelength area (mostly Fused Silica or CaF2).

... without consideration of the rear surface.

... with EBE coating technique for a good cost-performance ratio.

Customized coatings are available for all types.

 

–––– dashed lines show the zoomed curve with the stated magnification

AR 785-1030 nm / 0°
[B-07312]AR 785-1030 nm / 0°

785-1030 nm: R < 0.5%

HR 800 nm / 0° single stack
[B-06166]HR 800 nm / 0° single stack

800 nm: R > 99.8% single stack (quarter wave layers)

IF 780 nm / 6°
[B-06650]IF 780 nm / 6°

780 nm: FWHM 0.37 nm, best effort, angle tuning
(IBS-coating)

TFP 940 nm / 56°
[B-10213-01]TFP 940 nm / 56°

940 nm: Tp > 95%, Ts < 1% (IAD-coating)

VA 808 nm / 0-45° T 95-1%
[B-01476-01]VA 808 nm / 0-45° T 95-1%

808 nm: 0° -> 45°; T= 95% -> 1% (IAD-coating)

HR 905-945 nm HT 975-985 nm / 45°p
[B-05178]HR 905-945 nm HT 975-985 nm / 45°p

905-945 nm: Rp > 95%; 975-985 nm: Rp < 4%
(IBS-coating)